Fabrication and laser performance of highly transparent Nd:YAG ceramics from well-dispersed Nd:Y₂O₃ nanopowders by freeze-drying

摘要

Well-dispersed Nd:Y₂O₃ powders with uniform particle size of about 60 nm were synthesized from freeze-dried precursors. Highly transparent 2 at.% Nd:YAG ceramics were fabricated from the as-synthesized Nd:Y₂O₃ powders and commercial Al₂O₃ powders by vacuum sintering at 1,750 °C for 5 h. Phase evolution, microstructures, and spectroscopic properties of the Nd:YAG transparent ceramics were investigated. Freeze-drying played an important role in the synthesis of high-quality Nd:Y₂O₃ nanosized powders, which were essential for the fabrication of highly transparent Nd:YAG ceramics. Optical transmittance of a 3-mm thick sample reached 82% in the wavelength range of 200–900 nm. 5.23 W output power was obtained with 14.3 W diode laser pumping, giving a slope efficiency of 36.5%.