INFLUENZA DEL TRATTAMENTO TERMICO SULLE PROPRIETÀ MICROSTRUTTURALI E MECCANICHE DI LEGHE DI TITANIO DI TIPO BETA PER LA PRODUZIONE DI MOLLE

摘要

To evaluate the use of titanium alloys for helical spring production, an analysis of state of the art on β alloys and on manufacturing problems associated with titanium was carried out. The ability to substantially modify the mechanical properties of the alloy by tailored heat treatments is emphasised. Further, the necessity to control both hydrogen absorption and oxidation tendency as well as excessive grain growth during high temperature treatments (during solution treatment and hot working) is highlighted.%La memoria descrive le principali caratteristiche delle leghe β di titanio in relazione all'utilizzo nella fabbricazione di molle ad elica. Vengono discusse le proprietà del materiale al variare del trattamento termico, la possibilità di avvolgere le molle sia a caldo che a freddo e si affrontano le problematiche connesse con la forte reattività con l'ossigeno. La parte sperimentale descrive le caratteristiche microstrutturali e meccaniche effettivamente ottenibili al variare della temperatura di invecchiamento su una lega Ti-3AI-8V-6Cr-4Zr-4Mo. Viene valutata la resistenza al rilassamento delle molle e infine descritto il ciclo di fabbricazione per la produzione pilota di molle ad elica.