Effects of gage length, loading rates, and damage on the strength of PPTA fibers

摘要

Axial tension and transverse compression experiments on single fibers were performed to investigate the mechanical behavior of three high-performance fibers (Kevlar~®, Kevlar~® 129, and Twaron~®) with diameters in the order of 9-12 um. The single fibers were manufactured from 1998 through 2008. A miniaturized tensile Kolsky bar was used to determine the tensile response of PPTA single fibers at a high strain rate. Cage length and strain rate were found to have minimum effects on the tensile strength of PPTA single fibers. Manufacturing time over a decade was found to have negligible effects on the tensile strength of the fibers. Initial transverse compression on the fibers reduces their ultimate tensile strengths. A high resolution scanning electron microscope (SEM) was also used to examine the fracture modes of transversely deformed fibers. Different types of fracture morphology were observed.