摘要

We developed high voltage X-ray tubes using graphite field emitter inflamed at high temperature(GFEIHT). GFEIHT was fabricated from a graphite rod with a purity of 99.9 % which was inflamed in a hydrogen and oxygen gas mixture, with a gas ratio of hydrogen and oxygen of 2:1. The graphite surface had numberless nano-protrusions. We evaluated an electrical property of a GFEIHT cathode in an anode tube with a Be window. The anode current was to be 500 μA at voltage of 30 kV. The anode tube was tipped off under 10~(-7)Pa in order to fabricate an X-ray tube with the GFEIHT. A stability of this X-ray tube defined as variation coefficient(standard deviation/mean)of an anode voltage of 30 kV at a constant current of 500 μA was estimated to be 0.72 %.%高温燃焼グラフアイト電界放出源(Graphite field emitter inflamed at high temperature:GFEIHT)を用いた、高電圧駆動のX線管を開発した。GFEIHTは、高純度グラフアイト棒（99.9%)を水素-酸素混合炎(混合比2:1)中に曝露することにより作製される。その表面には、ナノサイズの突起が無数に存在している。GFEIHT陰極の電気特性を、ベリリゥムX線窓を有する硝子製の陽極管(内圧10~(-8)Pa台)にて評価したところ、陰極-陽極間電圧30kV時において500μA以上の電流を得た。この陽極管を10~(-7)Pa以下で封止し，X線管を作製した.このX線管の陽極電流を500と一定にしたときの陽極電圧(30 kV)の変動率(標準偏差/平均値)をX線管の安定度として定義し，これを求めることにより評価したところ，40時間以上の変動率は0.72%であった.