POSSIBILITY OF METAL COATINGS ON F82H AS THE TRITIUM PERMEATION REDUCTION BARRIER

摘要

Possibility of metal coatings on F82H as the tritium permeation reduction coating was examined by means of deuterium permeation experiment. Metal coatings such as copper, aluminum and gold plating of 10 μm thickness on outer surface of the F82H tube (250mm length, 10mm diameter and lmm thickness) were prepared as the permeation reduction coating. Permeation Reduction Factor (PRF) of the metal coatings was evaluated by comparing the steady state permeation flux between metal plated specimens and F82H specimen. As the results, the PRF of the metal coatings at 590K were 5, 100 and >1000 for copper, aluminum and gold plating, respectively. Those results indicate the possibility that aluminum and gold plating could be applied in the tritium system as the tritium permeation reduction method.