A novel coating layer on zirconia using modified zinc phosphatizing method

摘要

Yttria doped ZrO_(2) was deposited using an acidic zinc phosphatizing solution and the hydrothermal treatment. The coating was analyzed using a field emission-scanning electron microscope (FE-SEM), X-ray diffraction (XRD), energy-dispersive X-ray spectroscopy (EDX) and X-ray photoelectron spectroscopy (XPS). A piston on three balls (ISO 6872) was used for the measurement of biaxial flexural strength. MC3T3-E1 cells attachment was evaluated by SEM, and cell proliferation were assessed using MTS assay?. SEM images confirmed that the zinc phosphate coating layer was successfully prepared and fully covered the surface. The measured adhesive strength of the coating was 79.11 MPa. In vitro cell study indicated that the coated sample had better cell morphology and proliferation. XRD and EDS analysis revealed that the crystalline coating structure indexed as zinc phosphate (hopeite) and the substrate was assigned as zirconia. The flexural strength test showed that the strength of zirconia before and after hydrothermal treatment was not affected.