Effect of Phosphate on the Corrosion of Carbon Steel and on the Composition of Corrosion Products in Two-Stage Continuous Cultures of Desulfovibrio desulfuricans

摘要

A field isolate of Desulfovibrio desulfuricans was grown in defined medium in a two-stage continuous culture apparatus with different concentrations of phosphate in the feed medium. The first state (V1) was operated as a conventional chemostat (D = 0.045 h?1) that was limited in energy source (lactate) or phosphate. The second stage (V2) received effluent from V1 but no additional nutrients, and contained a healthy population of transiently starved or resting cells. An increase in the concentration of phosphate in the medium fed to V1 resulted in increased corrosion rates of carbon steel in both V1 and V2. Despite the more rapid corrosion observed in growing cultures relative to that in resting cultures, corrosion products that were isolated under strictly anaerobic conditions from the two culture modes had similar bulk compositions which varied with the phosphate content of the medium. Crystalline mackinawite (Fe9S8), vivianite [Fe3(PO4)2 · 8H2O], and goethite [FeO(OH)] were detected in amounts which varied with the culture conditions. Chemical analyses indicated that the S in the corrosion product was almost exclusively in the form of sulfides, while the P was present both as phosphate and as unidentified components, possibly reduced P species. Some differential localization of S and P was observed in intact corrosion products. Cells from lactate-limited, but not from phosphate-limited, cultures contained intracellular granules that were enriched in P and Fe. The results are discussed in terms of several proposed mechanisms of microbiologically influenced corrosion.