Synthesis and Characterization of Bi2Se3 Thermoelectric Nanopowders

摘要

In order to synthesize Bi2Se3 nanopowders by a solvothermal synthesis method, ethylenediamine, dimethylformamide,acetone, absolute ethanol, and deionized water were respectively used as a solvent, using BiCl3 and elemental Sepowders as starting materials and KBH4 as a reductant at 180oC for different times. X-ray diffraction was used for examiningthe phase composition of the products. The results showed that pure Bi2Se3 nanopowders were successfully synthesizedonly when deionized water was used as the solvent. Transmission electron microscopy observation revealed that thenanopowders consisted of big polygonal nanosheets and small irregular nanoparticles. The formation mechanism of theBi2Se3 nanosheets and nanoparticles was proposed.