Nanostructured CdS/CdSSe glass composite for photonic application

摘要

The present work describes the synthesis of CdS/CdSSe glass nanocomposites and its characterization. A few glass compositions were optimized and the optimized host glass was remelted along with different semiconductors like CdS and CdSSe at high temperature. The CdS/CdSSe is present in amorphous state in the glass matrix. The thermal treatments have been carefully optimized to obtain well-defined uniform crystal growth of CdS and CdSSe. The glasses with optimized conditions were fabricated and characterized thoroughly using UV, TG/DTA and TEM. The shift in absorption edge to the longer wavelength with heat treatment implies the increase in the crystal size. The band gap has been increased with decrease in the particle size. Crystal size of semiconductors obtained by TEM was 2.5-5 nm for the glass showing absorption edge cut-off at 475 nm (CM-475).