Study of the crystal structure of the high Tc superconductor Hg1-xRe xBa2Ca2Cu3O8+δ by using EXAFS, XANES and XRD

摘要

Hg based superconducting ceramics present the highest critical temperatures ever reported, particularly the phase 1223 with the highest Tc so far obtained -135 K. However, these compounds are obtained by a complex synthesis route and suffer degradation at ambient atmosphere. This disadvantage may be overcome by doping with an appropriate amount of Re. Samples of nominal composition Hg0.82Re0.18Ba2Ca2Cu3O8+δ having different oxygen contents were studied by X ray absorption and diffraction techniques. Using XANES we determined the Re valence = +7 in an octahedral distorted coordination. We determined the distances of Re-O bonds (1.85 ? and 2.10 ?) by EXAFS. XRD Rietveld fits showed segregation of two superconducting phases with distinct lattice parameters. The main phase is associated with Hg, Re-1223 with higher oxygen content, and the secondary superconducting phase is related to undoped Hg-1223.