Dissolution of lead matte and copper slag upon exposure to rhizosphere-like conditions

摘要

Metallurgical wastes displaying various chemical and mineralogical properties may reveal different behaviour under exposure to weathering conditions. The latter impact the stability of the wastes, which often results in metal release and subsequent pollution problems. The aim of this study was to compare the weathering of two types of metallurgical wastes (i.e., copper slag and lead matte) exposed to artificial root exudates organic solutions and demineralized water. The results of experimental weathering demonstrated that the extent of waste dissolution depends on the composition of weathering solution as well as on the waste properties. Artificial root exudates rich in organic acids were found to enhance elements release from sulphide rich lead matte and copper glassy slag relative to demineralized water control. The release of elements from the wastes exposed to artificial root exudates for 7 weeks reached 17.8% of Pb and 4.97% of Cu, for lead matte and granulated slag respectively. The most leachable elements may result from the dissolution of intermetallic phases hosting these elements. The fraction size ranging from 0.25–0.5 mm to 1–2 mm was found to be a minor factor in elements release under studied conditions.