Preparazione di supporti ceramici a base di fosfato naturale del Marocco per l'elaborazione di membrane di microfiltrazione e ultrafiltrazione

摘要

The preparation of new monotubular macroporous supports prepared from natural moroccan phosphates by extrusion process is reported. The characterization of the supports was performed by MEB to evaluate surface quality and mercury porosimetry for pore diameter. The surface morphology of supports fired at 1000 ℃ for 3 h does not show any macro defects and the supports show good final characteristics. The average pore diameter is near 70 μm and the porosity is about 43%. Filtration tests of a yeast suspension suggest suitability of these supports for microfiltration or ultrafiltration applications.%Viene descritta la fabbricazione di supporti macroporosi monotubolari innovativi, preparati a partire da fosfati naturali del Marocco, mediante processo di estrusione. La caratterizzazione dei supporti è stata eseguita tramite MEB per valutare la qualità della superficie, e con porosimetria a mercurio per misurare diametro dei pori. La morfologia della superficie dei supporti cotti a 1000 ℃ per 3 ore non presenta macro difetti e ì supporti evidenziano buone caratteristiche finali. Il diametro medio dei pori è attorno a 10 μm e la porosità circa 43%. I risultati delle prove di filtrazione di una sospensione di lievito, suggeriscono la possibilità che questi supporti siano idonei per applicazioni di micro filtrazione e ultrafiltrazione.