Hole transport parameters in a PTOPT based organic solar cell

摘要

The photovoltaic and charge transport properties of solar cells whose active layer is made from poly[3-(4-octylphenyl)-2, 2′-bithiophene](PTOPT) was studied. Devices are prepared in a sandwich-type structure of the form Al/PTOPT/PEDOT:PSS/ITO. The diodes showed good rectification needed for the PV cell. The symmetric nature of the semilogarithmic J-V plot under dark and low temperature reveals that there is a unipolar charge injection in both sides of the electrodes. Based on the space charge limited region J-V data, it was possible to study the electric field dependence of the hole transport, which enable us to derive important parameters such as the zero field mobility (μ_o) and the field activation factor (γ).Nous étudions les propriétés photovoltaïques et de transport de charge des cellules solaires dont la couche active est faite de poly [3-(4-octyphényle)-2, 2′-bithiophène] (PTOPT). Les dispositifs sont préparés selon une structure sandwich du type A1/PTOT/PEDOT:PSS/ITO. Les diodes ont de bonnes propriétés de rectification pour la cellule PV. La nature symétrique du graphique J-V sous faible éclairage et à basse température révèle qu'il y a injection d'une charge unipolaire des deux côtés des électrodes. Sur la base des données J-V dans la région limitée par les charges d'espace, il a été possible d'étudier la dépendance sur le champ électrique du transport de trous, ce qui nous permet d'obtenir d'importants paramètres comme la mobilité en champ nul (μ₀) et le facteur d'activation de champ (γ).