Microstructure evolution of eutectic Al-Cu strips by high-speed twin-roll strip casting process

摘要

In the present investigation, microstructural evolutions of functionally graded eutectic Al-Cu strips prepared by high-speed twin-roll strip caster at different casting speeds and liquid melt superheats were studied. The as-cast sample was subjected to scanning electron microscope to study the evolution of microstructure of the strip at different casting speeds and liquid melt superheats. At different casting speeds, non-equilibrium eutectic structure observed on the Al-Cu eutectic strip consists of lamellar as well as wavy structure with a distinct boundary. The lamellar microstructure consists of alternating layers of well-bonded α-Al phase and θ-Al_2Cu phase. The globular flowery structure within the eutectic matrix was observed on the strip at different liquid melt superheats. The microhardness of the as-cast strip was studied by Vickers hardness tester, and it was found that hardness value increases with increasing casting speed and decreases with increasing liquid melt superheat.