The color masking ability of a zirconia ceramic on the substrates with different values

摘要

>Background. The color masking ability of a restoration plays a significant role in coveringa discolored substructure; however, this optical property of zirconia ceramics has not been clearly determined yet. The aim of this in vitro study was to evaluate the color masking ability of a zirconia ceramic on substrates with different values.>Methods. Ten zirconia disk specimens,0.5 mm in thickness and 10 mm in diameter, were fabricated by a CAD/CAM system. Four substrates with different values were prepared, including: white (control), light grey, dark grey, and black. The disk specimens were placed over the substratesfor spectrophotometric measurements. A spectrophotometer measured the L^*, a^*, and b^* color attributes of the specimens. Additionally, ΔE values were calculated to determine the color differences between each group and the control,and were then compared with the perceptional threshold of ΔE=2.6. Repeated-measures ANOVA, Bonferroni, and one-sample t-test were used to analyze data. All the tests were carried out at 0.05 level of significance.>Results. The means and standard deviations of ΔE values for the three groups of light grey, dark grey and black were 9.94±2.11, 10.40±2.09, and 13.34±1.77 units, respectively.Significant differences were detected between the groups in the ΔE values (P<0.0001).The ΔE values in all the groups were more than the predetermined perceptional threshold(ΔE>2.6) (P<0.0001).>Conclusion. Within the limitations of this study, it was concluded that the tested zirconia ceramic did not exhibit sufficient color masking ability to hide the grey and black substrates.