Pyrochlore-type WO_3 powder was synthesized via hydrothermal method using aqueous sodium tungstate solution and oxalic acid as raw materials. The as-prepared powder was made into a soliquoid,from which films were made by dip coating process with indium-tin oxide(ITO).The obtained films were characterized by thermogravimetric and differential thermal analysis(TG-DTA), X-ray diffraction(XRD),scanning electron microscopy(SEM),transmission electron microscopy(TEM), cyclic voltammetry(CV), chronoamperometry(CA) and ultravioletvisible(UV-Vis) absorption. Results show that the crystal of the pyrochlore-type WO_3 powder is perfect. When the calcination temperature rises from room temperature to500 ℃,the pyrochlore-type structure first becomes deformed, then it is destroyed and turns into amorphous phase,finally it will completely convert to WO_3 with a monoclinic structure. Electrochemical and optical tests demonstrate that the film calcined at 300 ℃ exhibits the best electrochromic performance and has a coloration efficiency of up to 68.5 cm^2 C^(-1) at 884 nm.
展开▼
机译:The Application of the Golden Gate Image in Film and Television Media in History Teaching: Taking the Film "Summer Concerto" as an Example =影视媒体中的金门意象在历史教学的运用--以电影《夏天协奏曲》为例