Microstructure evolution of a new near-β titanium alloy:Ti555211 during high-temperature deformation

         

摘要

The isothermal compression testing of Ti555211 titanium alloys was carried out at deformation temperatures from 750 to 950 ℃ in 50 ℃ intervals,with strain rate of 0.001-1.000 s^(-1) and height reduction of 20%-60%.The effect of processing parameters(deformation temperature,strain rate and deformation degree) on the microstructure evolution and the microstructure variables was investigated.The results show that the content of primary α phase decreases with the increase in deformation temperature.The effect of strain rate on microstructure variables of isothermally compressed Ti555211 alloy is mainly dependent on the deformation temperature.The fine second α phase partly transforms to β phase due to the deformation heat effect at the high strain rate,α phase becomes globular with temperature increasing and strain rate decreasing.In contrast,α phase is refined with temperature decreasing and strain rate increasing.The deformation degree has a little influence on the grain size and the morphology of primary α phase,but the effect of deformation degree on the morphology of second α phase is significant.The larger deformation degree is in favor of the globularization of lamellar α structure.

著录项

相似文献

  • 中文文献
  • 外文文献
获取原文

客服邮箱:kefu@zhangqiaokeyan.com

京公网安备:11010802029741号 ICP备案号:京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有
  • 客服微信

  • 服务号