磷酸盐水泥基普通混凝土路面修补剂的研究

摘要

A kind of magnesium phosphate cement(MPC) cementing agent for the use of cement concrete pavement patching is researched. The main factora influencing final setting time and compressive strength of MPC were explored. The results show that the final setting time of the optimizing MPC samples reaches 20 min.thP compressive strength of samples cured for 3 d and 28 d reaches respectively 43 MPa and 62 MPa,and its bond strength reaches respectively 6.2 MPa and 8.6 MPa when MPC made by horax and magnesium oxide which has a surface area of 1889cm2/g.the mol ratio of disodium hydrogen phosphate and potassium dihydrogen phosphate to be 1/5.%研究了一种用于水泥混凝土路面修补用的磷酸镁水泥(MPC)胶结剂,探讨了影响磷酸镁水泥终凝时间和抗压强度的主要因素.结果表明,以比表面积为1889 cm2/g的氧化镁粉末,与磷酸氢二钠/磷酸二氧钾(摩尔比)=1/5复合,并掺加硼砂可以制备终凝时间20min,3d和28d抗压强度分别达43、62MPa,粘结强度达6.2、8.6 MPa的磷酸镁水泥.