An investigation was carried out of the resistance to cyclic oxidation of the as-castnormal-grained Co-30Cr-5Al alloy substrate at 1000℃ in air together with its sputteredcoating of microcrystallized CoCrAl alloy grains sized less than 0.5μm.Acoustie emissi oncounts showed that the initially formed Al2O3 scale on the bare alloy substrate cracked andspalled severely off after only one or two cycles on cooling and then the worse protective layerof Cr2O3 and CoCr2O4 spinel occurred on surface.While such substrate coated withsputtered microcrystallized CoCrAl alloy film was not damaged under oxidation even through100 cycles at 1000℃.In comparison with the normal-grained alloy,the microcrystallized al-loy,coating of similar constitution exhibite excellent resistance to oxide spalling on surface.