纳米晶复合Nd_(9.5)Fe_(76)Co_5Zr_(3-x)Nb_xB_(6.5)(x=0~3.0)粘结磁体的磁性能和温度系数的研究

     

摘要

采用熔体快淬法及真空退火工艺制备了Nd9.5Fe76Co5Zr3-xNbxB6.5(x=0~3.0)粘结磁体,研究了其磁性能及温度系数。结果表明,随着Nb含量的增加,合金剩磁逐渐提高,磁能积和矫顽力呈现先增大后减小的趋势。Zr元素与Nb元素复合添加,能够有效地改善矫顽力温度系数β。经最佳条件退火处理后制备的Nd9.5Fe76Co5Zr1.5Nb1.5B6.5的粘结磁体,具有最优的综合磁性能:Br=0.717T,Hcj=773kA/m,(BH)max=82kJ/m3,α20~150℃=-0.111%/℃,β20~150℃=-0.356%/℃。%Nanocomposite Nd_(9.5)Fe_(76)Co_5Zr_(3-x)Nb_xB_(6.5)(x=0~3.0) bonded magnets were prepared by melt-spun and vacuum annealing processes. The magnetic properties and temperature coefficients of the magnets were investi- gated. It could be found that the intrinsic coercivity and maximum energy product increased first, then de- creased, while the remanence increased with the increase of Nb addition for the Nd_(9.5)Fe_(76)Co_5Zr_(3-x)Nb_xB_(6.5)(x=0~3.0)magnets. The addition of Zr and Nb could improve obviously the temperature coefficient of coercivity. The optimal magnetic properties of bonded magnets were obtained for the nanocomposite Nd9.5Fe76 Co5 Zr1. 5 Nb1. 5 B6.5 magnet, that is Br = 0. 717T, Hcj = 773kA/m, (BH)max = 82kJ/ma, ae20-150℃ = - 0. 111%/℃, β20-150℃ = -0. 356 %//℃.

著录项

相似文献

  • 中文文献
  • 外文文献
  • 专利
获取原文

客服邮箱:kefu@zhangqiaokeyan.com

京公网安备:11010802029741号 ICP备案号:京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有
  • 客服微信

  • 服务号