高比表面积BaAl2O4粉体合成研究

摘要

BaAl2O4是优良的NOx存储催化剂材料,同时也是一种理想的荧光基体材料,受到了研究人员的广泛关注.但是一般的BaAl2O4粉体由于比表面积相对较小,使用受到了限制.虽然纳米颗粒有大的比表面积,但其团聚的缺陷严重限制了其应用.本文采用了一种简单的软模板法合成了BaAl2O4粉体.该粉体经过XRD表征表明为BaAl2O4,经BET表征具有较大比表面积.BaAl2O4粉体不仅化学稳定性好,而且具有相对较大的比表面积.其合成方法节省能源、生产效率高,在特定场合极有可能替代普通粉体做实际应用.%BaAl2O4 is an excellent NOx storage catalyst material. At the same time, it is also an ideal fluorescent matrix material and draws extensive attention. However, the general BaAl2O4 powder is limited by the relatively small surface area. Although the nanoparticles have larger surface area, the defect of their aggregation severely limits their applications. In this study, BaAl2O4 powder was synthesized by a simple soft template method, which not only had a good chemical stability, but also had a relatively large surface area. After characterizing by XRD, BET and TEM, the powder proved exactly the BaAl2O4 with a larger surface area. The synthesis method in this paper has high production efficiency and energy efficiency, and the powder is likely to replace the commonly-used powder on particular occasions.