Effects of high-pressure rheo-squeeze casting on the Fe-rich phases and mechanical properties of Al-17Si-(1,1.5)Fe alloys

摘要

The effects of high pressure rheo-squeeze casting(HPRC) on the Fe-rich phases(FRPs) and mechanical properties of Al-17 Si-(1,1.5)Fe alloys were investigated. The alloy melts were first treated by ultrasonic vibration(UV) and then formed by high-pressure squeeze casting(HPSC). The FRPs in the as-cast HPSC Al-17 Si-1 Fe alloys only contained a long, needle-shaped β-Al5 Fe Si phase at 0 MPa. In addition to the β-Al5 Fe Si phase, the HPSC Al-17 Si-1.5 Fe alloy also contained the plate-shaped δ-Al4 Fe Si2 phase. A fine, block-shaped δ-Al4 Fe Si2 phase was formed in the Al-17 Si-1 Fe alloy treated by UV. The size of FRPs decreased with increasing pressure. After UV treatment, solidification under pressure led to further refinement of the FRPs. Considering alloy samples of the same composition, the ultimate tensile strength(UTS) of the HPRC samples was higher than that of the HPSC samples, and the UTS increased with increasing pressure. The UTS of the Al-17 Si-1 Fe alloy formed by HPSC exceeded that of the Al-17 Si-1.5 Fe alloy formed in the same manner under the same pressure. Conversely, the UTS of the Al-17 Si-1 Fe alloy formed by HPRC decreased to a value lower than that of the Al-17 Si-1.5 Fe alloy formed in the same manner.