目的 确定局部环境谱当量加速关系.方法 以×型飞机某半封闭关键部位为研究对象,依据其在机体中所处的位置及服役环境中各气候条件编制局部加速腐蚀试验环境谱,分别进行试验室周期浸润加速腐蚀和自然环境暴晒.借助涂层宏观、微观形貌检测、色差、光泽度等常规性能检测和电化学极化曲线测试,对两种不同环境下试验件进行性能测试.结果 试验室周期浸润加速腐蚀196.6h,相当于舰面停放1年,且经过实验室2个周期加速腐蚀与自然环境暴晒2年的试验件涂层形貌、失光率、色差、电化学性能一致.结论 该局部环境谱当量加速关系准确可靠.%Objective To determine the equivalent accelerated relationship of local environment spectrum.Methods A semi closed key part of an aircraft was researched.Environment spectrum of local accelerated corrosion test was compiled based on its location in the plane and climate conditions of the service environment to carry out laboratory immersion corrosion and environmental exposure respectively:Test pieces of two different environments were tested for performance according to general performance test on macro and micro topography detection,color difference,gloss and other properties.Results Accelerated corrosion of cycle immersion in library for 196.6 hours was equivalent to parking on the ship surface for 1 year.The coating morphology,light loss rate,color difference,and electrochemical performance of two cycles of accelerated corrosion in laboratory were consistent with two years of natural exposure.Conclusion The equivalent accelerated relationship of the local environmental spectrum is accurate and reliable.
展开▼