针对难降解物质壬基酚聚氧乙烯醚的特性拟开发一种新型介孔碳材料对其进行吸附处理.采用软模板法合成介孔碳,并针对壬基酚聚氧乙烯醚的特性,在合成过程中添加六亚甲基四胺,制备出介孔碳-NH2吸附材料,并将其吸脱附性能与介孔碳材料进行对比.结果显示:对于介孔碳材料来说,最适吸附剂量为0.04 g/L,最适壬基酚聚氧乙烯醚初始质量浓度为800 mg/L,最适转速为200 r/min,最适pH值为3.对于介孔碳-NH2来说,最适吸附剂量为0.08 g/L,最适壬基酚聚氧乙烯醚初始质量浓度为800 mg/L,最适转速为200 r/min,最适pH值为3.准一级方程用于拟合介孔碳及介孔碳-NH2对壬基酚聚氧乙烯醚的吸附过程更为符合实际实验.介孔碳及介孔碳-NH2的吸附等温线用Freundlich方程拟合更为准确.并且介孔碳-NH2具有最优的再生性和最优的吸附效果.%In this paper, mesoporous carbon adsorbents for wastewater treatment were applied for the characteristics of refractory materials. Soft template was used to synthesis mesoporous carbon, and modified mesoporous carbon was made according to the characteristics of NPEOs in this method by adding hexamethylene tetramine during the synthesis of mesoporous carbon-NH2, the modified mesoporous carbon was obtained. The influences of different adsorption conditions were optimized. For mesoporous carbon, the optimums of adsorbent dose, NPEOs initial concentration, rotating speed, and pH were 0.04 g/L, 800 mg/L, 200 r/min, and 3, respectively. Mesoporous carbon-NH2 showed the highest NPEOs adsorption capacity at adsorbent dose of 0.08 g/L, NPEOs initial concentration of 1000 mg/L, rotating speed at 1000 r/min, and Ph at 3. Lagergren adsorption kinetics fitted mesoporous carbon and mesoporous carbon-NH2 adsorption of NPEOs accuratly. And Freundlich was more accurate than the Langmuir model for mesoporous carbon and mesoporous carbon-NH2. Moreover, mesoporous carbon-NH2 has more excellent reproduction stability and optimal adsorption effects than mesoporous carbon.
展开▼