The ferrites of Cuo-ZnO-Fe2o3 solid solution series near the molar ratio of ZnxCu1-x were prepared by direct heating of their coprecipitated hydroxides using NH4OH as precipitating agent where x=0.0, 0.2, 0.5, 0.8 and 1.0. Additional amounts of Cu and Zn sulphates were added to compensate the loss during the coprecipitation of the hydroxides. The ferritized samples were characterized by chemical analysis, XRD. DTA, TGA and SEM. XRD of both Zn0.2Cu0.8Fe2O4 and Zn0.5Cu0.5 Fe2O4 that indicates the formation of a heterogeneous ferrite material of ZnFe2O4 and CuFe2O4 mixed with variable amounts of α-Fe2O3. Zn and Cu ferrites were observed only in Zn0.8Cu0.2Fe2O4.From TGA-time relation, the activation energy of the different transformation phases were calculated. It is found that, the activation energy of ZnFe2O4 is slightly equal to 3/2 of that for CuFe2O4. Dielectric measurements show that the electrical behaviour depends on the ordering and disordering of the phases.
展开▼
机译:Stratigraphic characterization of ancient Roman frescos by laser induced breakdown spectroscopy and importance of a proper choice of the normalizing lines
机译:How the Group Leaders of Lesson Preparation Groups Facilitate Group Learning and Reflective Practice in Chinese Public High Schools =中国公立高中的备课组长是如何引领团队学习和反思性实践的?
机译:preparation and characterization of imidazolium-functionalized poly (ether sulfone) as anion exchange membrane and ionomer for fuel cell application