Densified Yb-,Y-,Dy-,Sm- and Nd-α-Sialon ceramics were prepared by two-step hot sintering.The variation of microstructure and properties with different rare-earth was investigated.The ceramics doped with smaller cations (Yb^(3+),y^(3+) and Dy^(3+)) are fully composed ofα-Sialon,while in the larger cations (Sm^(3+) and Nd^(3+)) doped ceramics also exist a few intergranular phase M′(Re_2Si_(3-x)Al_xO_(3+x)N_(4-x)) in triple-point pockets.With increasing the radius of the rare-earth cations,the elongatedα-Sialon grains form instead of the equiaxed grains in Yb-α-Sialon,and the aspect ratio of grains increases.All the ceramics possess high hardness and the value of 21 GPa is achieved for Yb- and Y-α-Sialon.With increasing the ionic size of rare-earth the hardness decreases slightly but the toughness tends to increase.Nd-α-Sialon possesses the highest toughness with the value of 5.4 MPa.m^(1/2).
展开▼
机译:Espectroscopiadeconstacânciaemicroestrutura devitrocerâmicasLi1+ x [al xGe2-x(pO4)3]coníonslítioImpedancespectroscopy and microstructure of lithium conductor Li1 + x [al xGe2-x(pO4)3] glass ceramics