Silicone/graphene oxide co-cross-linked aerogels with wide-temperature mechanical flexibility,super-hydrophobicity and flame resistance for exceptional thermal insulation and oil/water separation

摘要

Development of multifunctional and high-performance silicone aerogel is highly required for various promising applications.However,unstable cross-linking structure and poor thermal stability of silicone network as well as complicated processing restrict the practical use significantly.Herein,we report a facile and versatile ambient drying strategy to fabricate lightweight,wide-temperature flexible,super-hydrophobic and flame retardant silicone composite aerogels modified with low-content functionalized graphene oxide(FGO).After optimizing silane molecules,incorporation ofγ-aminopropyltriethoxysilane functionalization is found to promote the dispersion stability of GO during the hydrolysis-polymerization process and thus produce the formation of unique strip-like co-cross-linked network.Consequently,the aerogels containing∼2.0 wt%FGO not only possess good cyclic compressive stability under strain of 70%for 100 cycles and outstanding mechanical reliability in wide temperature range(from liquid nitrogen to 350℃),but also display excellent flame resistance and super-hydrophobicity.Further,the optimized silicone/FGO aerogels display exceptional thermal insulating performance superior to pure aerogel and hydrocarbon polymer foams,and they also show efficient oil absorption and separation capacity for var-ious solvents and oil from water.Clearly,this work provides a new route for the rational design and development of advanced silicone composite aerogels for multifunctional applications.