(La0.2Ce0.2Nd0.2Sm0.2Eu0.2)2Zr2O7:A novel high-entropy ceramic with low thermal conductivity and sluggish grain growth rate

摘要

Fine grains and slow grain growth rate are beneficial to preventing the thermal stress-induced cracking and thermal conductivity increase of thermal barrier coatings.Inspired by the sluggish diffusion effect of high-entropy materials,a novel high-entropy(HE)rare-earth zirconate solid solution(La0.2Ce0.2Nd0.2Sm0.2Eu0.2)2 Zr2 O7 was designed and successfully synthesized in this work.The as-synthesized(La0.2Ce0.2Nd0.2Sm0.2Eu0.2)2 Zr2 O7 is phase-pure with homogeneous rare-earth element distribution.The thermal conductivity of as-synthesized(La0.2Ce0.2Nd0.2Sm0.2Eu0.2)2 Zr2 O7 at room temperature is as low as 0.76 W m^-1 K^-1.Moreover,after being heated at 1500℃for 1-18 h,the average grain size of(La0.2Ce0.2Nd0.2Sm0.2Eu0.2)2 Zr2 O7 only increases from 1.69μm to 3.92μm,while the average grain size of La2Zr2O7 increases from 1.96μm to 8.89μm.Low thermal conductivity and sluggish grain growth rate indicate that high-entropy(La0.2Ce0.2Nd0.2Sm0.2Eu0.2)2Zr2O7 is suitable for application as a thermal barrier coating material and it may possess good thermal stress-induced cracking resistance.