High strength and ductility Mg-8Gd-3Y-0.5Zr alloy with bimodal structure and nano-precipitates

摘要

To resolve the strength-ductility trade-off problem for high-strength Mg alloys,we prepared a high performance Mg-8Gd-3Y-0.5 Zr(wt%)alloy with yield strength of 371 MPa,ultimate tensile strength of 419MPa and elongation of 15.8%.The processing route involves extrusion,pre-deformation and aging,which leads to a bimodal structure and nano-precipitates.Back-stress originated from the deformationincompatibility in the bimodal-structure alloy can improve ductility.In addition,dislocation density in coarse grains increased during the pre-deformation strain of 2%,and the dislocations in coarse grains can promote the formation of chain-like nano-precipitates during aging treatment.The chain-like nanoprecipitates can act as barriers for dislocations slip and the existing mobile dislocations enable good ductility.