仿生合成羟基锡酸锌包覆碳酸钙及其对PVC的阻燃研究

摘要

Taking sodium dodecyl benzene suffonate(SDBS)as the template in the water solution, zinc hydroxystannate-coated calcium carbonate (ZHSCC-1)was prepared by biominetic synthesis method, and zinc hydroxystannate-coated calcium carbonate (ZHSCC-2)was also prepared in water solution without SDBS. Both ZHSCC-1 and ZHSCC-2 were studied as the flame retardant of PVC. The results showed that, when ZHSCC at the same addition level, not only the flame retardant and smoke suppressant effects of ZHSCC-1 were better than those of ZHSCC-2, but also the beneficial effects of the former were better than those of the latter.%采用仿生合成的方法,以十二烷基苯磺酸钠(SDBS)为模板,在水溶液中制备了羟基锡酸锌包覆碳酸钙(ZHSCC-1),并将其和不添加SDBS模板制备的羟基锡酸锌包覆碳酸钙(ZHSCC-2)分别应用在PVC 中进行对比研究.结果表明:在ZHSCC含量相同时,ZHSCC-1对PVC的阻燃消烟效果明显优于ZHSCC-2,且前者对PVC的拉伸强度、断裂伸长率、抗冲强度的有益影响都优于后者.