FORMABILITY OF MAGNESIUM SHEET ZE10 AND AZ31 WITH RESPECT TO INITIAL TEXTURE

摘要

The commercial application of magnesium alloy sheets is hindered by their low formability and therefore technological and economic constraints. Tailoring the texture has been identified as playing a major role in enhancing the formability of magnesium sheets. In this study, the formability of magnesium sheet ZE10 and AZ31 was investigated. While the texture of AZ31 is of unfavourable basal type, ZE10 shows a significantly different texture with the basal planes being randomly distributed. More basal planes are oriented favourably for basal slip, promising higher formability and thus, lower process temperature. Formability is assessed by means of forming limit diagrams as a representation of material response to various strain paths. Nakajima tests were carried out from room temperature to 250℃. Local strain data is correlated with the microstructural evolution. This study reveals a significant influence of texture on formability with ZE10 sheet showing superior formability compared to AZ31.