The Effect of Increased Waste Loading on the Durability of High Level Waste Glass.

摘要

This paper describes the results from static leach tests using the ASTM International standard Materials Characterisation Centre (MCC-1) and Product Consistency Test (PCT) protocols for inactive High Level Waste (HLW) glasses fabricated at full scale on the Sellafield Vitrification Test Rig. The samples comprised monoliths and powders of a 75:25 OxiderMagnox Blend glass with 31 wt％ waste incorporation and a Magnox-only glass with 35 wt％ waste incorporation. The tests were carried out in de-ionized water at 90 ℃ for durations up to 42 days and normalized mass losses calculated.rnThe results of MCC-1 and PCT tests on both 31 wt％ Blend and 35 wt％ Magnox glasses, showing measurable differences to the corresponding standard 25 wt％ waste incorporation glasses, are presented. A series of Scanning Electron Microscopy (SEM) investigations were also undertaken. The variation in composition and thickness of the alteration layer with sample type and duration is reported.