Crystalline Organic Semiconducting Thin Films Cast from a Novel Thermolytic Thiophene Oligomer

摘要

Here we report on OTFTs made from a novel thermoresponsive thiophene based oligomer. The functionalized oligomer is soluble in common solvents, but loses its solubility upon thermolysis. Devices with channel lengths from 5 to 40 urn were fabricated from solution then subjected to thermolysis at temperatures ranging from 150-250 °C. The initially amorphous materials reorganize into highly crystalline films upon thermolysis. Crystallinity was characterized by x-ray diffractometry and atomic force imaging. AFM studies depicted the nucleation of molecular terraces, where the formation and overall height of terraces was observed to be dependent upon the thermolysis temperature and solvent choice. These factors con-elated to overall performance. For both dip-cast and spin-cast samples, devices were fabricated at a process temperature of 180 °C with mobilities of 0.07 cm~2/Vs and on/off ratios > 105. The devices were relatively stable in both air and common solvents, with their mobility degrading only by -25% upon immersion in the original casting solvents. The solubility characteristics and process temperatures for these devices may be particularly suitable for solution processing on flexible substrates.