Corrosion behavior of Aluminium-Boron carbide-Graphite composites

摘要

The corrosion behaviour of Al (6061)-B4C-Graphite was investigated. The Aluminium Metal Matrix Composites (AMMC) was fabricated through two step stir casting method. The composites were fabricated with various volume percentages of Boron Carbide (5, 10 &15%) and Graphite (5, 10& 15%). Corrosion studies of AMMC was investigated with 4%, 8%, 12% wt.% NaCl solution at room temperature. Also erosion-corrosion test were performed on the specimens in the NaCl solution with silica sand. Erosion-corrosion tests indicated that the rate of material loss mechanism is mechanical abrasion with enhanced corrosion. The material loss mechanism was significantly higher in the case of erosion-corrosion tests.