Low-Temperature Combustion Synthesis of Cordierite Powder and Its Characteristic

摘要

The MgO-Al_2O_3-SiO_2 (MAS) glass powders have been synthesized by low-temperature combustion technique using magnesium nitrate, aluminium nitrate, silicic acid as material, urea as fuel. The crystallization process, sintering behavior and dielectric properties were investigated by means of DTA, XRD, TMA and SEM techniques. The results showed that the glass powders could be sintered at lower than 1000°C. The μ-cordierite phase was first crystallized from glass and then transformed into α-cordierite phase during sintering process. The obtained cordierite-based glass-ceramics at 950°C and 1000°C have low dielectric constant (4.00 ～ 4.96 at 1 MHz), low dielectric dissipation factor (≈ 0.003) and high sintering density (which is above 98% of the theoretical density), which are used for electronic packaging.