INDENTATION MODULUS AND YOUNG'S MODULUS OF CU-CR-ZR ALLOY AT MACRO-SCALE LEVEL

摘要

In this communication the first experimental results of indentation modulus and Young's modulus (tensile modulus) of seven samples of Cu-Cr-Zr alloy (chemical composition: 1%Cr, 0.06%Zr, rest Cu), in the macro-scale range at room temperature, are presented and compared.