One of the major considerations in the current deep drawing practice is the product quality. In this research, the effect of heating temperature on the drawability of the round metal cup has been investigated. Firstly, round metal cups of aluminium and mild steel were drawn from the blank diameters of 60 mm, 65 mm and 70 mm. The experiment conducted at room temperature first, then at 50°C and 100°C. The elongation of the major and minor strains along the cup profile after the process is measured and analysed. On the other hand, the defects from the experiment output and ABAQUS/CAE simulation are compared. The result from experiment shows that the highest major elongation is 11.64 mm and it is happened to a deep drawn aluminium round cup with LDR of 1.69 at temperature of 100°C. On the other hand, for deep drawn mild steel round cup, shows highest major elongation of 12.44 mm for a cup with LDR of 1.56 at 100°C. Both of these statements indicates that the higher temperature could improve the formability of the deep drawn parts besides reducing the probability of the defect to be happened.
展开▼