Densification Mechanism of Al_2O_3/Al Metallic Ceramics Prepared via Powder Metallurgy Method

摘要

Alumina ceramics with good mechanical and corrosion resistance, is one of the most widely used engineering ceramics. The aluminum has a high strength, high conductivity, high plasticity, etc. than aluminum ceramics used in more and more industries. In this paper, aluminum and alumina powder as raw material, mixing, forming, sintering and a series of processes for preparing the alumina/aluminum metallic ceramic materials, through performance testing and analysis can be found in the ratio of raw materials 50wt% Al, 50wt % Al_2O_3 relatively good moldability. After sintering, after measuring the density contrast is found better density in the pressing process pressure of 20MPa and holding pressure time for 20min. By comparing the sintering process, after the interface structure by scanning electron microscopy and found help improve density through the secondary sintering metallic ceramic materials.