Synthesis and Characterization of Monodisperse Core-shell Lanthanide Upconversion Nanoparticles NaYF4: Yb,Tm/SiO2

摘要

Lanthanide up-converting luminescent nanoparticles(UCNPs)are exciting and promising materials for optical bioimaging,biosensor and theranostic due to their unique and advantageous optical and chemical properties.The UCNPs absorb low energy near-infrared(NIR)light and emit high-energy shorter wavelength photons(visible light).Their unique features allow them to overcome various problems associated with conventional imaging probes such as photostability,lack of toxicity,and to provide versatility for creating nanoplatforms with both imaging and therapeutic modalities.This paper reports synthesis and characterization of core-shell structured of NaYF4:Yb,Tm/SiO2 microspheres.The synthesis of lanthanide upconversion nanoparticles NaYF4:Yb,Tm was prepared by thermal decomposition process which involves dissolving organic precursors in high-boiling-point solvents oleic acid(OA)and octadecene(ODE).After that,the NaYF4:Yb,Tm phosphors was coated by silica via reverse microcrnulsion process to obtain core-shell structured NaYF4:Yb,Tm/Si02.Scanning electron microscopy,transmission electron microscopy,specific area electron diffraction,and photolumincscence were applied to characterize these samples.The obtained core-shell structured NaYF4:Yb,Tm/Si02 phosphors exhibit a perfect cubic morphology with narrow size distribution and smooth surface.Upon 1R excitation at 980 nm,the NaYF4:Yb,Tm/SiO2 samples exhibit whitish blue upconversion(UC)luminescence,respectively.These phosphors show potential applications in the displaying on biological fields and biosensing.