The effect of loading direction on the dwell fatigue properties of Ti-6Al-4V forged bar with highly oriented texture

摘要

The purpose of this study was to improve our understanding of the effect of macro/micro texture on dwell fatigue properties. The Ti-6Al-4V forged bar with highly oriented texture and fine equiaxed microstructure was used. Dwell fatigue, cyclic fatigue and creep tests were conducted at room temperature by using specimens taken in the longitudinal (L) direction and the transverse (T) direction of the bar. The effects of loading direction on dwell fatigue life and fracture surface morphology were examined in detail. The dwell fatigue life in T direction was shorter than that in L direction. The fracture surface morphologies were characteristically varied by loading waveform, amplitude and directions. In the range of 93 - 95% of 0.2%PS, the characteristic large facets were observed in the T direction in dwell fatigue. Detailed analyses revealed that the large facet consists of multiple initiation facets and propagation facets. The propagation facet plane and crack propagation direction appeared to correspond to alpha (0001) <10-10>. Furthermore, the relationship between strain rate and life time was compared to that for room temperature creep. The deviation from the Monkman-Grant relationship corresponded to the change of the fracture surface morphology.