Effect of Rare Earth on High Temperature Properties of Heat-resisting Steel

摘要

The oxidation resistance and high temperature mechanical properties of FeCrNi heat-resisting steel are analyzed and studied. The results show that the oxidation resistance of the heat-resisting steel is improved remarkably after adding RE. The value of oxidation rate of Sample 1 (without adding RE) is 1.71 times higher than Sample 2, respectively at 1423K. And the value of oxidation rate of Sample 1 is 1.4 times higher than Sample 2, respectively at 1473K. The fracture mode of heat-resisting stainless steel is typical cleavage fracture, but dimple fracture after adding RE into the steel. The high temperature mechanical properties of heat-resisting steel is improved obviously by RE. In comparison with heat-resisting stainless steel without RE, the reduction of area of heat-resisting stainless steel with RE is increased 26.27% at 1123K.