Effects of solution and cryogenic treatments on microstructures and mechanical properties of AZ31 alloy tubes

摘要

In order to improve plastic property of AZ31 alloy tubes at room temperature and expand application of cold rolling process in magnesium (Mg) alloys, solution treatment (T4) and cryogenic treatment of AZ31 tubes obtained by drawing were investigated in this work. The results indicate that T4 can improve the microstructure of the alloy, refine grains and eliminate twins. The optimized T4 parameter is 300 °C for 8 h, in which the average grain size of 12 μm can be obtained and elongation reaches to Max of 16.1% and tensile strength reaches to 242 MPa. Moreover, tensile strength was decreased to 211 MPa, while, elongation was improved to 25.4% by T4+cryogenic treatment at -196 °C.