Soft magnetic property of Fe_(80)Ni_(20)-O/ZnO_n multilayer thin films for high-frequency application

摘要

A series of [Fe_(80)Ni_(20)-O/ZnO]_n multilayer thin films with different ZnO separate layer thicknesses (t, from 0 to 3 nm) and fixed Fe_(80)Ni_(20)-O/ZnO layer thickness (about 5 nm) have been fabricated on (lOO)-oriented silicon wafers and glass substrates by reactive magnetron sputtering. Microstructure analysis and static magnetic measurement results indicate that the magnetic properties of the films can be adjusted by the variation of ZnO monolayers thickness. All films reveal an evident in-plane uniaxial magnetic anisotropy (IPUMA). The values of in-plane uniaxial magnetic anisotropy fields (Hk) and resistivity (p) can be changed from 8 to 57 Oe and 62 to 168 ì?-cm respectively with the t increasing. While the values of hard axis coercivity (H_(ch),) and easy axis coercivity (H_(ce)) reveal minimums of 1.5 and 3 Oe respectively at t = 1 nm.