The influence of fluoride on stress corrosion cracking (SCC) of NiTi orthodontic wires was investigated using slow strain rate test (SSRT) and scanning electron microscopy (SEM). The results indicated that fluoride significantly accelerated the stress corrosion cracking of NiTi orthodontic wires. The fractographies of NiTi orthodontic wires exhibited striation pattern.

机译：使用慢菌速率试验（SSRT）和扫描电子显微镜（SEM）研究了氟化氟对NITI正畸线应力腐蚀裂纹（SCC）的影响。结果表明，氟化物显着加速了Niti正畸线的应力腐蚀裂纹。 NITI正畸电线的分数表现出抗条纹图案。

著录项

来源
《International Conference on Frontiers in Materials Science and Technology》|2008年||共4页
会议地点
作者
Xiaoji Li; Jianqiu Wang; En-hou Han; Wei Ke;
展开▼
作者单位

展开▼
会议组织
原文格式 PDF
正文语种
中图分类 TB3-53;
关键词
NiTi orthodontic wire; Fluoride; Slow strain rate test; Stress corrosion cracking;

机译：NITI正畸丝;氟化物;慢应变率测试;应力腐蚀裂纹;

相似文献

外文文献
中文文献
专利

1. Comparative study on corrosion behaviour of Nitinol and stainless steel orthodontic wires in simulated saliva solution in presence of fluoride ions [J] . M. Mirjalili, M. Momeni, N. Ebrahimi, Materials science & engineering . 2013,第4期

机译：氟离子存在下镍钛诺和不锈钢正畸丝在模拟唾液中的腐蚀行为比较研究
2. Stress corrosion cracking of solution annealed austenitic stainless steel type 304 in sulfuric acid-sodium chloride solution --effects of NaCl concentration and chromate [J] . Rokuro Nishimura, Koji Yamakawa 材料 . 1999,第11期

机译：溶液退火奥氏体不锈钢型304硫酸 - 氯化钠溶液中的应力腐蚀裂纹 - NaCl浓度和铬酸钠
3. Stress corrosion cracking of solution annealed austenitic stainless steel type 304 in sulfuric acid-sodium chloride solution --effects of NaCl concentration and chromate [J] . Rokuro Nishimura, Koji Yamakawa 材料 . 1999,第11期

机译：硫酸-氯化钠溶液中的304退火奥氏体不锈钢的应力腐蚀开裂-NaCl浓度和铬酸盐的影响
4. Stress Corrosion Cracking of NiTi Orthodontic Wires in Sodium Fluoride Solution [C] . Xiaoji Li, Jianqiu Wang, En-hou Han, International Conference on Frontiers in Materials Science and Technology . 2008

机译：氟化钠溶液中NITI正畸线的应力腐蚀裂纹
5. THE EFFECT OF STRESS ON STRESS-CORROSION CRACKING OF SOME AUSTENITIC STAINLESS STEEL WIRES IN BOILING 42 WT. PERCENT MAGNESIUM-CHLORIDE AQUEOUS SOLUTION. [D] . HAWKES, HORACE PEARL, JR. 1962

机译：应力对沸腾42 WT的某些奥氏体不锈钢钢丝应力腐蚀开裂的影响。氯化镁水溶液。
6. Assessment of the electrochemical behaviour of Nickel-Titanium-based orthodontic wires: Effect of some natural corrosion inhibitors in comparison with fluoride [O] . Nassiba Fatene, Said Mansouri, Bouchra Elkhalfi, 2019

机译：镍钛基正畸丝的电化学行为评估：与氟化物相比某些天然腐蚀抑制剂的作用
7. Corrosion. Stress Corrosion Cracking of Solution Annealed Austenitic Stainless Steel Type 304 in Sulfuric Acid-Sodium Chloride Solution. Effects of NaCl Concentration and Chromate. [O] . Rokuro NISHIMURA, Koji YAMAKAWA 1999

机译：腐蚀。溶液退火奥氏体不锈钢型304在硫酸钠溶液中的应力腐蚀开裂。 NaCl浓度和铬酸盐的影响。
8. Stress Corrosion Cracking of Titanium Alloys Studies of Cracks in Thin Specimens Scc of Ti-6AL-4V IN Chloride, Iodide and Fluoride Solutions Stress Corrosion Cracking in Molten Salts Electrochemistry of Freshly Generated Titanium Surfaces [R] . Beck, T. R., Blackburn, M. J., Smyrl, W. H. 1971

机译：钛合金应力腐蚀开裂Ti-6aL-4V在氯化物，碘化物和氟化物溶液中的薄试样scc裂纹研究熔盐中的应力腐蚀开裂新生钛表面的电化学

Stress Corrosion Cracking of NiTi Orthodontic Wires in Sodium Fluoride Solution

摘要

著录项

引文网络

相似文献

相关主题

期刊订阅