Isothermal oxidation behavior of HVAF-sprayed NiCoCrAlY coatings: Effect of surface treatment

摘要

NiCoCrAlY coatings are widely used as bond coats for ceramic thermal barrier coatings (TBCs) and oxidation and corrosion protective overlay coatings in industrial gas turbines. High temperature oxidation behaviour of NiCoCrAlYs has a great influence on the coating performance and lifetime of TBCs. A promising route to decrease the oxidation rate of such coatings is post-coating surface modification which can facilitate formation of a uniform alumina scale with a considerably slower growth rate compared to the as-sprayed coatings. In this work, the effect of surface treatment by means of shot peening and laser surface melting (LSM) on the oxidation resistance of high velocity air-fuel (HVAF) sprayed NiCoCrAlY coatings was studied. Isothermal oxidation was carried out at 1000°C for 1000h. Results showed that the rough surface of as-sprayed HVAF sprayed coatings was significantly changed after shot peening and LSM treatment, with a compact and smooth appearance. After the exposure, the oxide scales formed on surface-treated NiCoCrAlY coatings showed different morphology and growth rate compared to those formed on as-sprayed coating surface. The oxidation behaviour of surface treated HVAF-sprayed NiCoCrAlY coatings were revealed and discussed.