Casting of High Aluminum Content AM Series Magnesium Alloys by Using a Horizontal Twin Roll Caster

摘要

In this paper, twin roll casting of magnesium alloys with high aluminum content such as, Mg-11 mass%Al-0.2 mass%Mn, Mg-12 mass%Al-0.2 mass%Mn, Mg-13 mass%Al-0.2 mass% have been performed for the purpose of use as an original material for hot forging. Also the mechanical properties of the cast materials were examined. A 10 miri-meters thick strip was cast by the use of a horizontal twin roll caster. The microscopic observation was conducted to investigate into the precipitation of the metal compounds such as Mg17Al12, and the Vickers hardness of the cast strips test were performed. From the result of the roll casting experiments, a 10 mm thick strip was continuously cast at a roll speed of 3.1 m/min. The average grain size of the casting strips was about 46 micron meters. When the aluminum content was 13%, the hardness of the twin roll cast (TRC) strips became 1.7 times higher than that of extruded AZ 31. Also, a uniaxial compression test at elevated temperature was conducted to obtain a true strain-true stress curve for examining possibility of direct hot forging (DHF) of TRC magnesium alloys with high aluminum content.