Low Cycle Fatigue Life Evaluation According to Temperature and Orientation in Nickel-Base Superalloy

摘要

Components of gas turbines must be extremely resistant to high temperatures, high stresses, high-temperature corrosion, and erosive environments. The materials used in these environmental conditions are mainly nickel-based superalloys. In this study, the low-cycle fatigue of the nickel-based superalloy Inconel 792 was examined. The total strain range of a gas turbine between 760 °C and 870 °C was considered as the parameter representing the actual gas turbine operation. In addition, tests were performed using a trapezoidal waveform of the total strain to reflect the operation-stop conditions of a gas turbine with frequent shutdowns. The results of the fatigue test were compared with the Coffm-Manson method and energy method. The fractured surface was analyzed using a scanning electron microscope (SEM).