INFLUENCE OF LONG-TERM ANNEALING ON RESIDUAL STRESS DISTRIBUTION AND QUASI-BRITTLE FAILURE PROPERTIES OF TALCUM REINFORCED PIPE GRADE POLYPROYPLENE

摘要

In this study a polypropylene material with talcum reinforcement used for sewer pipes has been subjected to an annealing procedure at 80°C, roughly 60°C above the actual application temperature, in air for a time period of 18 months. As expected, examination of the material showed no significant decrease in mechanical or fracture mechanical properties due to the temperature exposure. However, samples stored at higher temperature showed better resistance against quasi-brittle failure in fatigue tests compared to unconditioned samples. This could mainly be attributed to the decrease of residual stress in the pipe wall. Even though pipes have been annealed for very long times above Tg, residual stress could not be totally relaxed within 18 months.