DISCUSSION OF DELIVERED CONDITION SPECIFIED IN ASME CODE CASE 2702 ON INCONEL 740H USED FOR A-USC BOILER

摘要

Delivered condition of Inconel740H specified in ASME Code Case 2702 is solution heat treated and aged condition, fabricating performances are also based on the condition, and a re-annealing and aging shall be performed if cold forming to strains is over 5%. These almost harsh requirements bring great inconvenience for its engineering practice and utilization. The comparative bending tests on 740H tubes in solution heat treated + aged condition and solution heat treated condition were performed, and the rules' reasonability of the specification on delivered condition was discussed and analyzed from point view of deformability and weldability in the paper. The bending test results showed that tube bent was difficult because of its high strength and limited deforming capacity in solution heat treated + aged condition. Therefore, the material supplied in the solution condition may be better from fabricating points. Whether re-solution for the bent tube is performed after bending depends on its bending radius, followed by welding and post weld heat treatment of component (this treatment can also be the aging treatment for annealed sector at the same time), this treating manner can meet regulatory requirements. For solution tubes, however, there are some inconveniences to its engineering application because fewer researches were carried out on its properties up to now, and no regulations on them were given for the material in the specification. Suggestions are: 1) deeply investigating the properties of tubes in solution condition, including mechanical and fabricating performances, 2) adding the mechanical properties, maximum allowable cold forming to stain without performing re-solution and weld strength reduction factor of solution material to the code case.