Corrosion Behaviours of Mo Modified Ti6AI4V Alloy in Hank's Solution

摘要

The Mo surface modified layer on Ti6Al4V alloy was obtained by the plasma surface alloying technique. The structure and composition of the Mo modified Ti6A14V alloy was investigated by X-ray diffraction (XRD) and glow discharge optical emission spectroscopy (GDOES). The Mo modified layer contains Mo coating on subsurface and diffusion layers between the subsurface and substrate. The X- ray diffraction analysis of the Mo modified Ti6Al4V alloy reveals that the outmost surface of the Mo modified Ti6Al4V alloy is composed of pure Mo. The electrochemical corrosion performance of the Mo modified Ti6A14V alloy in 25 °C Hank's solution was investigated and compared with that of Ti6A14V alloy. Results indicate that the self-corroding electric potential and the corrosion-rate of the Mo modified Ti6A14V alloy are higher than that of Ti6A14V alloy in 25°C Hank's solution.